Electrodeposited Ni–B alloy coatings: Structure, corrosion resistance and mechanical properties
By Bekish, Yu.N.; Poznyak, S.K.; Tsybulskaya, L.S. & Gaevskaya, T.V.
Published in Electrochimica Acta
2010
Abstract
Ni–B alloy coatings with different boron content ranging from 4 to approximately 28 at.% were prepared by electrodeposition in a nickel-plating bath containing sodium decahydroclovodecaborate as a boron source. The influence of the boron concentration in the coatings on their structure, morphology, electrochemical and corrosion behavior, physico-mechanical and electrical properties was investigated using X-ray diffractometry (XRD), scanning electron microscopy (SEM), potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and other methods. It was found that the electrodeposited Ni–B coatings with relatively low boron content (≤8 at.%) are nanocrystalline and comprise a solid solution of boron in f.c.c. Ni lattice having a mixed substituted-interstitial type. Further increase in the boron content (up to 10–15 at.%) leads to the appearance of heterogeneous amorphous-nanocrystalline structure, and the coatings with a high boron content (20 at.% and above) are X-ray amorphous. Polarization measurements in neutral NaCl solutions showed that the Ni–B coatings with relatively low boron content demonstrate a potential region of low anodic currents associated with the passive film formation at the alloy surface. The anodic current in this potential region increases significantly with increasing the boron content above 10 at.%, suggesting the non-protective nature of the anodic film formed on the amorphous Ni–B alloys. Immersion tests monitored by EIS measurements revealed a significantly better corrosion performance of the Ni–B coatings with low boron content (4 at.%) in comparison with that of the amorphous coatings. The microhardness and wear resistance of the Ni–B coatings essentially increases with increasing the boron content. Maximum microhardness and wear resistance were found for the coatings containing 8 at.% B.