Formulation and evaluation of nano-structured polymeric coatings for corrosion protection
By Aglan, Anwar; Allie, Aldinton; Ludwick, Adriane & Koons, Lawrence
Published in Surface and Coatings Technology
2007
Abstract
The effect of the addition of multi-walled carbon nano-tubes (MWCNT) to epoxy and vinyl chloride/vinyl acetate copolymer coatings on their ability to protect the substrates was studied. Coatings were formulated from these resins with and without MWCNT reinforcement. Steel substrates were prepared and coated with each formulated coating and submerged in 5% NaCl solution to study their corrosion resistance by means of Electrochemical Impedance Spectroscopy (EIS). In addition, thin films from these polymers, with and without nano-reinforcement, were cast. Dogbone specimens were cut in order to study their mechanical properties. Some of these specimens were immersed in the NaCl solution for two weeks in order to compare their mechanical properties with samples not exposed to salt water. Optical microscopy was used to capture the progress of sample corrosion. EIS measurements showed that the addition of MWCNTs to epoxy and vinyl chloride/vinyl acetate copolymer (VYHH) coatings increased their charge transfer resistance in comparison with the neat coatings. This is an indication of the enhanced corrosion protection of the nano-coatings. In addition, mechanical strength tests, both before and after immersion in 5% NaCl solution, showed that thin films from both epoxy and VYHH resins containing MWCNTs had improved strength, an indication of an improvement in the coatings' cohesive properties.