Novel Sulfonated Co-poly(ether imide)s Containing Trifluoromethyl, Fluorenyl and Hydroxyl Groups for Enhanced Proton Exchange Membrane Properties: Application in Microbial Fuel Cell
By Kumar, Anaparthi Ganesh; Singh, Asheesh; Komber, Hartmut; Voit, Brigitte; Tiwari, Bikash Ranjan; Noori, Md. Tabish; Ghangrekar, Makarand M.; Banerjee, Susanta
Published in ACS Applied Materials & Interfaces
2018
Abstract
A hydroxyl group containing new cardo diamine monomer was synthesized, namely 9,9-bis (hydroxy- (4?-amino(3-trifluoromethyl)biphenyl-4-oxy)-phenyl)-9H-fluorene (mixture of isomers, HAPHPF). HAPHPF, along with a sulfonated diamine monomer, 4,4?-diaminostilbene-2,2?-disulfonic acid (DSDSA), was used to prepare a series of new sulfonated copolyimides by polycondensation with 1,4,5,8-naphthalenetetracarboxylic dianhydride (NTDA). The degree of sulfonation (DS < 1) was adjusted by the feed ratio of DSDSA/HAPHPF and the copolymers were named as DHN-XX, where XX denotes the mole percentage of DSDSA (XX = 50, 60, and 70). The copolymers showed high molecular weights. The copolymer structure and composition were confirmed by FTIR and NMR techniques. Copolymer membranes were prepared through solution cast route by using dimethyl sulfoxide as a solvent. The membranes showed high thermal, mechanical, hydrolytic and peroxide radical stability, and low water uptake and low swelling ratios. Well-separated hydrophilic and hydrophobic phase morphology was observed in TEM and AFM images of the copolymer membranes and was further supported by the SAXS studies. The proton conductivity of the DHN-70 was as high as 97 mS cm