Optimization of USSP duration for enhanced corrosion resistance of AA7075
By Pandey, Vaibhav; Singh, J. K.; Chattopadhyay, K.; Srinivas, N. C. Santhi; Singh, Vakil
Published in Ultrasonics
2019
Abstract
This investigation was carried out following our earlier work on the effect of ultrasonic shot peening (USSP) on corrosion resistance of the 7075 aluminium alloy in 3.5 wt% NaCl solution to optimize the duration of USSP. The samples not treated with USSP and different samples treated with USSP were subjected to potentiodynamic polarization and electrochemical impedance spectroscopy. Among the specimens USSP treated from 5 to 30 s, the one USSP treated for 15 s (USSP 15) was found to exhibit highest corrosion potential (Ecorr) and lowest corrosion current density (icorr). Corrosion products were characterized by Scanning Electron Microscopy (SEM) and X-ray Photoelectron Spectroscopy (XPS). Scanning Kelvin Probe Force Microscopy (SKPFM) was used to measure the surface free potential. The enhanced corrosion resistance of the USSP 15 sample was found to be due to combined effect of surface nanostructure of the matrix, homogeneity and refinement of second phase precipitates. There was enhancement in formation of adherent passive layer in the USSP15 specimen.