ZnSxSe1-x/N-C (x = 0.24) hierarchical nanosphere with improved energy storage capability as sodium-ion battery anode
By Cao, Dongxu; Wang, Yuyu; Kang, Wenpei; Li, Chenxu; Cao, Dongwei; Fan, Lili; Wang, Rongming; Sun, Daofeng
Published in Journal of Alloys and Compounds
2019
Abstract
Anode materials are demonstrated to essentially affect the electrochemical performance of sodium-ion batteries (SIBs), which are considered as a promising large-scale energy storage device. In this work, alloying ZnSxSe1-x (x = 0.24) and N doped carbon composite (ZnSxSe1-x/N-C (x = 0.24)) hierarchical nanospheres are prepared by selenizing the ZnS precursor. The corresponding X-ray diffraction and high-resolution transmission electron microscopy results prove the formation of an alloyed phase, resulting in a wider lattice compared with ZnS. Benefitting from the coexistence of S2? and Se2? in the ZnSxSe1-x lattice, the weaker Zn-Se bonds and wider lattice spacing facilitate ultrafast pseudocapacitive sodium storage capability and enhanced cycling stability, when ZnSxSe1-x/N-C is used as anode material for SIBs. At current of 1.0 A g?1, it delivers a capacity of 378 mAh g?1 after 130 cycles with capacity retention of 87.9%, which is much higher than 34.3% for the ZnS/N-C electrode. In addition, for the rate performance, it can maintain an impressive capacity of 233 mAh g?1 at 10.0 A g?1 with a capacity retention of 55.9% in comparison with the capacity at 0.2 A g?1. This work provides us common thoughts to enhance the electrochemical performance of transition metal chalcogenide anode through anion substitution.