MOF-derived porous hollow ?-Fe2O3 microboxes modified by silver nanoclusters for enhanced pseudocapacitive storage
By Yu, Zhuying; Zhang, Xingyan; Wei, Lu; Guo, Xin
Published in Applied Surface Science
2019
Abstract
Porous hollow ?-Fe2O3 microboxes with high surface area are prepared by using metal-organic framework as precursor and self-template. To improve the conductivity of the derived ?-Fe2O3 microboxes and thus enhance their capacitive storage and rate capability as effective electrode material, especially as anode material for supercapacitors, Ag nanoclusters are uniformly deposited on the surface of the ?-Fe2O3 microboxes (?-Fe2O3@Ag microboxes) through a facile solution method. As pseudocapacitive material, the ?-Fe2O3@Ag microbox electrode displays a high specific capacitance of 701 F g?1 at a current density of 0.1 A g?1, and remains 191 F g?1 at a high current density of 10 A g?1. Furthermore, the material shows 80% specific capacitance retention after 2000 charge-discharge cycles, and 72% retention after 10,000 cycles at a current density of 10 A g?1. In addition, asymmetric supercapacitors are assembled with the ?-Fe2O3@Ag as negative electrodes and commercial activated carbon as positive electrodes. A maximum specific capacitance of 123 F g?1 and an energy density of 41.8 W h kg?1 are demonstrated within a cell voltage of 1.6 V for the device.