Antibacterial durability and biocompatibility of antibacterial-passivated 316L stainless steel in simulated physiological environment
By Zhao, Jinlong; Zhai, Zhaofeng; Sun, Da; Yang, Chunguang; Zhang, Xinrui; Huang, Nan; Jiang, Xin; Yang, Ke
Published in Materials Science and Engineering: C
2019
Abstract
Stainless steel (SS) has been widely applied as one of the most efficient implant metal materials, although corrosion and infection in body environment are still challenging. Herein, an antibacterial passivation method was employed to enhance the antibacterial performance and corrosion resistance of the medical 316L SS. The result proved that the antibacterial-passivated 316L SS exhibited stable antibacterial activity and effectively inhibited the formation of bacterial biofilm. Electrochemical measurements combined with X-ray photoelectron spectroscopy technique were used to study the corrosion resistance and semiconductor behavior of passivated 316L SS immersed in simulated physiological environment. The results indicated that the 316L SS after antibacterial passivation treatment for 1 h, soaking in the medium for 10 days, showed satisfactory corrosion resistance attributing to proper Cu deposition in the passive film. The anodic stripping voltammetry measurement further confirmed that the Cu-bearing passive film could continuously release Cu ions into medium. The zebrafish test demonstrated an excellent in vivo biocompatibility for the 316L SS with antibacterial passivation for 0.5 and 1 h, respectively. In addition, changes of surface roughness, contact angle and chemical composition after antibacterial passivation played an important role in explaining the antibacterial mechanism, which could be clearly divided into contact killing and ionic release killing. Hence, the antibacterial passivation treatment was preliminarily proved as a potential way for enhancing the persistent antibacterial activity and corrosion resistance of 316L SS.